TF-241 P et N fundatae flammae retardant fontes carbonis continentes pro polyolefin, HDPE
Introductio
Core commoda mixtionis APP TF 241. flammam retardat in polypropylene (PP) haec sunt.
Primo, TF-241 flammabilitatem PP efficaciter supprimit, augens eius incendium resistentiam.Hoc pendet in applicationibus ubi salus ignis est prioritas.
Secundo TF-241 optimam stabilitatem habet scelerisque, structuralem integritatem PP sub calidis temperaturis servans.Etiam adiuvat reducere fumum emissiones et emissiones gas toxicus in combustione, casus sanitatis potentiae diminuentes.
Praeterea TF compatibilitas cum PP 241 eximius est, ut facilem integrationem et congruentem obtineat effectum.
Super, synergistica mixtura TF-241 nucleum suum commoda demonstrat ut flamma retardans PP.
Specifications
| Specification | TF-241 |
| Aspectus | Pulvis albus |
| P content (w/w) | ≥22 % |
| N content (w/w) | ≥17.5% |
| pH valorem (10% aq, ad 25℃) | 7.0~9.0 |
| Viscositas (10% aq, 25℃) | 30mPa·s |
| umor (w/w) | -0.5% |
| Magnitudo (D50) | 14~20µm |
| Magnitudo particula (D100) | 100µm |
| Solubilitas (10% aq, ad 25℃) | 0.70g/100ml |
| Decomposition Temperature (TGA, 99%) | ≥270℃ |
Characteres
1. Halogen-liberi et nulli gravis metalli ions.
2. Humilis densitas, humilis fumus generatio.
3. Pulvis albi, resistentia aquae bonae, transire potest 70℃, immersio test 168h .
4. Princeps stabilitatis scelerisque, effectus processus bonus, nullae lapsus aquae manifestus in processu
5. Minima addita moles, flamma alta efficientiam retardat, plus quam 22% transire potest UL94V-0 (3.2mm)
6.Flame-retardantes fructus habent bonam observantiam caliditatis resistentiae et transire possunt GWIT 750℃ et GWFI 960℃ probationes
7.Biodegradable in phosphoro et nitrogenio composita
Applications
TF-241 adhibetur in homopolymerizatione PP-H et copolymerizatione PP-B et HDPE.Vulgo in flamma retardant polyolefin et HDPE sicut vaporis aeris calefacientis et domestici adjumenta.
Applicationem dux
Relatio formula pro 3.2mm PP (UL94 V0);
| Materia | Formula S1 | Formula S2 |
| Homopolymerization PP (H110MA) | 77.3% |
|
| Copolymerization PP (EP300M) |
| 77.3% |
| Ducatus (EBS) | 0.2% | 0.2% |
| Facilisis (B215) | 0.3% | 0.3% |
| Anti-distillantia (FA500H) | 0.2% | 0.2% |
| TF-241 | 22-24% | 23-25% |
Proprietates mechanicas fundatae in 30% additamento voluminis TF-241.Cum 30% TF-241 ad UL94 V-0 perveniret (1.5mm)
| Item | Formula S1 | Formula S2 |
| Vertical flammability rate | V0 (1.5mm) | UL94 V-0 (1.5mm) |
| Finis oxygeni index (%) | 30 | 28 |
| Roboris distrahentes (MPa) | 28 | 23 |
| Prolongatio in confractus (%) | 53 | 102 |
| Flammabilitas rate cum aqua cocta (70℃, 48h) | V0 (3.2mm) | V0 (3.2mm) |
| V0 (1.5mm) | V0 (1.5mm) | |
| Modulus flexilis (MPa) | 2315 | 1981 |
| Index solve (230℃,2.16KG) | 6.5 | 3.2 |
Stipare:25kg/bag, 24mt/20'fcl sine grabatis, 20mt/20'fcl cum cursare.Alia stipare petentibus.
Repono:in sicco et frigido loco, humido et sole arcendo, min.pluteo duos annos vivere.